Loctite® Fixmaster® 235626 PC 7222 2-Part Wear Resistant Putty, 1 lb Kit, Paste Part A/Solid/Paste Part B Form, Dark Gray Part A, Gray Part B, Part A: 1.07/Part B: 2.228

  • Manufacturer: Henkel
  • Brand Name: Loctite®
  • Part Number: LOC98742
  • MPN: 235626
  • UPC: 079340987425
  • Min. Order Qty: 1
  • Qty. Interval: 1
    • Sign In for Pricing and Availability

Loctite® Fixmaster® Wear Resistant Putty, 2-Part, Series: PC 7222, Kit Container, 1 lb Container, Epoxy Base, Composition: Part A: Aluminum Oxide, Diethylenetriamine, Alkyl Phenol, Silicon Dioxide, Epoxy Polyamine Adduct, 4,4'-Isopropylidenediphenol, Triethylenetetramine, Substituted Piperazine, Titanium Dioxide, Aluminum, Alkyl Phenol, Benzyl Alcohol, Benzyldimethylamine ; Part B: Silicon Carbide, Epoxy Resin, Aluminum Oxide, Treated Fumed Silica, Cristobalite, Carbon Black, Aluminum, Paste Part A/Solid/Paste Part B Form, 342 sq-cm at 6 mm THK/0.45 kg Coverage, 30 min Application Time, 6 hr Curing, Dark Gray Part A, Gray Part B, Part A: Ammoniacal, Part B: Slight/Epoxy Odor/Scent, -30 to 105 deg C, Part A: 1.07/Part B: 2.228 Specific Gravity, Part A: > 93 deg C, Part B: 250 deg C Flash Point, 2:1 By Volume/2:1 By Weight Mixing Ratio, Applicable Materials: Aluminum, Brass, Concrete, Iron, Plastic, Steel, Wood, 3020 psi Tensile Strength, 2440 psi Shear Strength

Applicable Materials      :      Aluminum, Brass, Concrete, Iron, Plastic, Steel, Wood
Application Time      :      30 min
Base Type      :      Epoxy
Color      :      Dark Gray Part A, Gray Part B
Composition      :      Part A: Aluminum Oxide, Diethylenetriamine, Alkyl Phenol, Silicon Dioxide, Epoxy Polyamine Adduct, 4,4'-Isopropylidenediphenol, Triethylenetetramine, Substituted Piperazine, Titanium Dioxide, Aluminum, Alkyl Phenol, Benzyl Alcohol, Benzyldimethylamine ; Part B: Silicon Carbide, Epoxy Resin, Aluminum Oxide, Treated Fumed Silica, Cristobalite, Carbon Black, Aluminum
Container Size      :      1 lb
Container Type      :      Kit
Coverage      :      342 sq-cm at 6 mm THK/0.45 kg
Curing Time      :      6 hr
Flash Point      :      Part A: > 93 deg C, Part B: 250 deg C
Form      :      Paste Part A/Solid/Paste Part B
Mixing Ratio      :      2:1 By Volume/2:1 By Weight
Odor/Scent      :      Part A: Ammoniacal, Part B: Slight/Epoxy
Series      :      PC 7222
Shear Strength      :      2440 psi
Specific Gravity      :      Part A: 1.07/Part B: 2.228
Temperature Rating      :      -30 to 105 deg C
Tensile Strength      :      3020 psi
Type      :      2-Part
  • Item Features 01=Ceramic fibers that give this trowelable putty excellent wear and abrasion resistant properties under typical dry service temperatures of -29 to 107 deg C
  • Item Features 02=Provides smooth, low friction finish for equipment exposed to wear, erosion, and cavitation
  • Item Features 03=Renews worn surfaces fast reduces downtime
  • Item Features 04=Small ceramic bead filled resists fine particle sliding abrasion, prolongs equipment life
  • Item Features 05=D 89 shore hardness
  • Item Features 06=45 to 55 gel time at 25 deg C
  • Item Features 07=Epoxy hardener part A, epoxy resin part B